Low Cement Castables
Royal Mon - 50
Royal Mon - 50 by Royal Refractories. Dense low-cement castables engineered for high strength, controlled water demand, and service temperatures from 1500°C to 1700°C.
Weight: 25 Kg Bag
Technical Properties
| Service Temp | 1500°C |
| Grain Size | max 6 mm |
| Bulk Density110 Min | 2.35 g/cc |
| CCS110 | 650 Kg/cm² |
| CCS1100 | 800 Kg/cm² |
| CCS1400 | 1000 Kg/cm² |
| PLC1400 | +/-1.0% |
Chemical Analysis
| Al2O3 | 49% |
| Fe2O3 | 1.5% |
Additional Information
| Recommended Water | 6.5-7.5% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Typical applications
- • Monolithic furnace linings
- • High-strength hot-face linings
- • Kiln and foundry refractory construction
Related Low Cement Castables
Technical Properties
| Service Temp | 1500°C |
| Grain Size | max 6 mm |
| Bulk Density110 Min | 2.20 g/cc |
| CCS110 | 650 Kg/cm² |
| CCS1100 | 750 Kg/cm² |
| CCS1400 | 900 Kg/cm² |
| PLC1400 | +/-1.0% |
Chemical Analysis
| Al2O3 | 43% |
| Fe2O3 | 1.5% |
Additional Information
| Recommended Water | 6.5-7.5% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Technical Properties
| Service Temp | 1600°C |
| Grain Size | max 6 mm |
| Bulk Density110 Min | 2.40 g/cc |
| CCS110 | 650 Kg/cm² |
| CCS1100 | 800 Kg/cm² |
| CCS1400 | 1000 Kg/cm² |
| PLC1400 | +/-1.0% |
Chemical Analysis
| Al2O3 | 58-60% |
| Fe2O3 | 1.5% |
Additional Information
| Recommended Water | 6-7% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Technical Properties
| Service Temp | 1600°C |
| Grain Size | max 6 mm |
| Bulk Density110 Min | 2.75 g/cc |
| CCS110 | 750 Kg/cm² |
| CCS1100 | 850 Kg/cm² |
| CCS1400 | 1000 Kg/cm² |
| PLC1400 | +/-1.0% |
Chemical Analysis
| Al2O3 | 70% |
| Fe2O3 | 1.6% |
Additional Information
| Recommended Water | 5.5-6.5% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Need help confirming this grade for your lining requirement? Contact Royal Refractories for technical and quotation support.