Product category
Low Cement Refractory Castables
Dense low-cement castables for high-strength monolithic linings, with grades rated up to 1850°C.
Typical applications
- • Monolithic furnace linings
- • High-strength hot-face linings
- • Kiln and foundry refractory construction
Technical Properties
| Service Temp | 1850°C |
| Grain Size | max 5 mm |
| Bulk Density (110°C) | 3200 kg/m³ (3.20 g/cc) |
| Bulk Density (850°C) | 3150 kg/m³ |
| CCS (1600°C) | 100 MPa |
| Thermal Conductivity (1600°C) | 4.3 W/m·K |
| PLC (1600°C) | 0 to 0.4% |
| Country of Origin | India |
Chemical Analysis
| Al2O3 | 98% |
| Fe2O3 | 0.05% |
Additional Information
| Shelf Life | 24 months |
Technical Properties
| Service Temp | 1500°C |
| Grain Size | max 6 mm |
| Bulk Density (110°C, minimum) | 2.20 g/cc |
| CCS (110°C) | 650 Kg/cm² |
| CCS (1100°C) | 750 Kg/cm² |
| CCS (1400°C) | 900 Kg/cm² |
| PLC (1400°C) | +/-1.0% |
Chemical Analysis
| Al2O3 | 43% |
| Fe2O3 | 1.5% |
Additional Information
| Recommended Water | 6.5-7.5% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Technical Properties
| Service Temp | 1500°C |
| Grain Size | max 6 mm |
| Bulk Density (110°C, minimum) | 2.35 g/cc |
| CCS (110°C) | 650 Kg/cm² |
| CCS (1100°C) | 800 Kg/cm² |
| CCS (1400°C) | 1000 Kg/cm² |
| PLC (1400°C) | +/-1.0% |
Chemical Analysis
| Al2O3 | 49% |
| Fe2O3 | 1.5% |
Additional Information
| Recommended Water | 6.5-7.5% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Technical Properties
| Service Temp | 1600°C |
| Grain Size | max 6 mm |
| Bulk Density (110°C, minimum) | 2.40 g/cc |
| CCS (110°C) | 650 Kg/cm² |
| CCS (1100°C) | 800 Kg/cm² |
| CCS (1400°C) | 1000 Kg/cm² |
| PLC (1400°C) | +/-1.0% |
Chemical Analysis
| Al2O3 | 58-60% |
| Fe2O3 | 1.5% |
Additional Information
| Recommended Water | 6-7% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Technical Properties
| Service Temp | 1600°C |
| Grain Size | max 6 mm |
| Bulk Density (110°C, minimum) | 2.75 g/cc |
| CCS (110°C) | 750 Kg/cm² |
| CCS (1100°C) | 850 Kg/cm² |
| CCS (1400°C) | 1000 Kg/cm² |
| PLC (1400°C) | +/-1.0% |
Chemical Analysis
| Al2O3 | 70% |
| Fe2O3 | 1.6% |
Additional Information
| Recommended Water | 5.5-6.5% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Technical Properties
| Service Temp | 1700°C |
| Grain Size | max 6 mm |
| Bulk Density (110°C, minimum) | 2.75 g/cc |
| CCS (110°C) | 750 Kg/cm² |
| CCS (1100°C) | 1000 Kg/cm² |
| CCS (1450°C) | 1200 Kg/cm² |
| PLC (1450°C) | +/-0.8% |
Chemical Analysis
| Al2O3 | 80% |
| Fe2O3 | 1.85% |
Additional Information
| Recommended Water | 5-6% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |
Technical Properties
| Service Temp | 1700°C |
| Grain Size | max 6 mm |
| Bulk Density (110°C, minimum) | 3.00 g/cc |
| CCS (110°C) | 800 Kg/cm² |
| CCS (1100°C) | 900 Kg/cm² |
| CCS (1450°C) | 1200 Kg/cm² |
| PLC (1450°C) | +/-0.8% |
Chemical Analysis
| Al2O3 | 88% |
| Fe2O3 | 0.7% |
Additional Information
| Recommended Water | 4.5-5.5% |
| Mixing Time | 5-8 min |
| Shelf Life | 6 months |